It is not toxic The first fact and the most important is Polymer clay or Fimo is perfectly safe around children and pets, as it is non-toxic. This means that there is no need to worry about toxic fumes when baking polymer clay in the oven, nor does it need to panic if a child pretends to eat a polymer clay dumpling.
Can you paint polymer clay?
Polymer clay doesn’t shrink or expand as it cures, meaning you can paint it before you bake. Unbaked clay may create a better bond with paint as it cures. Test different types and brands of paint to find the best results.
How long does FIMO last?
If it is stored correctly, polymer clay lasts indefinitely (a decade or longer). However, it can dry out and it’s possible to ruin it under certain conditions. Before talking about how to tell whether your clay is beyond help and how you may be able to save it, it’s helpful to know what polymer clay is.
Is FIMO safe?
Several companies, such as FIMO, switched to other plasticizers well before this date. Many major brands of polymer clay now use a citrate based plasticizer. It is non-toxic, biodegradable, and safe to use in children’s toys, medical products, and any sort of PVC.
How do you tell if your polymer clay is done?
Bake for 15 minutes per quarter inch of thickness. For example, a piece of 1/2″ thickness should be cured for 30 minutes. To test the curing, try pressing the tip of your fingernail into the bottom of your piece after it has cooled; it will leave a mark but will not actually enter the clay.
Can polymer clay be used for food?
It is perfectly safe to cure or bake polymer clay in your home oven. If you burn polymer clay, small amounts of irritating vapor can be emitted, so ventilate the room if this happens. Manufacturers cannot certify their material for making food utensils, so polymer clay is not certified to be used for food contact.
Can you put polymer clay in water?
As polymer clay is a waterproof oil based material it can get wet, either in it’s baked or unbaked state. Water can however make the clay a little more brittle, if a design is submerged after baking.